Skip to page content
USDA Forest Service
  
Treesearch

Research & Development Treesearch

 
Treesearch Home
About Treesearch
Contact Us
Research & Development
Forest Products Lab
International Institute of Tropical Forestry
Northern
Pacific Northwest
Pacific Southwest
Rocky Mountain
Southern
Help
 

GeoTreesearch


Science.gov - We Participate


USA.gov  Government Made Easy


Global Forest Information Service

US Forest Service
P.O. Box 96090
Washington, D.C.
20090-6090

(202) 205-8333

You are here: Home / Search / Publication Information
Bookmark and Share

Publication Information

(360 KB)

Title: Effects of fire retardants on physical, mechanical, and fire properties of flat-pressed WPCs

Author: Ayrilmis, Nadir; Benthien, Jan T.; Thoemen, Heiko; White, Robert H.

Date: 2012

Source: European journal of wood and wood products. Vol. 70, nos. 1/3 (Jan. 2012): p. 215-224.

Publication Series: Miscellaneous Publication

Description: Physical, mechanical, and fire properties of the flat-pressed wood plastic composites (WPCs) incorporated with various fire retardants (10% by weight) at different levels of wood flour (WF) content, 40, 50, or 60 wt%, were investigated. The WPC panels were made from dry-blended WF, polypropylene (PP), and fire retardant (FR) powders with maleic anhydride-grafted PP (2 wt%) formulations using a conventional flat-pressing process under laboratory conditions. Incorporation of the fire retardants into the WPC panels significantly decreased the internal bond strength compared to the WPC panels without FR at all levels of the WF content. The modulus of rupture of the WPC panels containing FRs decreased with the increase in the WF content from 40 to 60 wt%. The modulus of elasticity increased with the increase in the WF content from 40 to 50 wt% and then decreased as the WF content reached 60 wt%. The WPC panels incorporated with zinc borate gave an overall best performance in both physical and mechanical properties followed by the panels treated with decabromodiphenyl oxide, magnesium hydroxide, and ammonium polyphosphate. Higher levels of the WF content resulted in significantly improved fire resistance of the WPC panels with and without FR as measured in the cone calorimeter. Of the four fire retardants tested, ammonium polyphosphate showed the most improvement over untreated ones.

Keywords: Fireproofing agents, composite materials, fire testing, testing, wood-plastic composites, polypropylene, thermoplastic composites, wood flour, mechanical properties, maleic anhydride, moisture, adsorption, heat release rate, fire hazard, fire retardants, flat pressing, moisture content, strength, zinc borate, magnesium hydroxide, flammability, fire resistance, thermal degradation, cone calorimetry, ammonium polyphosphate, bonding, bond strength, decabromodiphenyl oxide

Publication Notes:

  • We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
  • This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.

XML: View XML

Citation:


Ayrilmis, Nadir; Benthien, Jan T.; Thoemen, Heiko; White, Robert H. 2012. Effects of fire retardants on physical, mechanical, and fire properties of flat-pressed WPCs. European journal of wood and wood products. Vol. 70, nos. 1/3 (Jan. 2012): p. 215-224.

 


 [ Get Acrobat ]  Get the latest version of the Adobe Acrobat reader or Acrobat Reader for Windows with Search and Accessibility

USDA logo which links to the department's national site. Forest Service logo which links to the agency's national site.