Skip to page content
USDA Forest Service
  
Treesearch

Research & Development Treesearch

 
Treesearch Home
About Treesearch
Contact Us
Research & Development
Forest Products Lab
International Institute of Tropical Forestry
Northern
Pacific Northwest
Pacific Southwest
Rocky Mountain
Southern Research Station
Help
 

GeoTreesearch


Science.gov - We Participate


USA.gov  Government Made Easy


Global Forest Information Service

US Forest Service
P.O. Box 96090
Washington, D.C.
20090-6090

(202) 205-8333

You are here: Home / Search / Publication Information
Bookmark and Share

Publication Information

(366 KB bytes)

Title: Effects of processing method and moisture history on laboratory fungal resistance of wood-HDPE composites.

Author: Clemons, Craig M.; Ibach, Rebecca E.

Date: 2004

Source: Forest products journal. Vol. 54, no. 4 (Apr. 2004): Pages 50-57.

Publication Series: Miscellaneous Publication

Description: The purpose of this study was to clarify the effects of composite processing and moisture sorption on laboratory fungal resistance of wood-plastic composites. A 2-week water soaking or cyclic boiling-drying procedure was used to infuse moisture into composites made from high-density polyethylene filled with 50 percent wood flour and processed by extrusion, compression molding, or injection molding. Extruded composites absorbed the most moisture; compression-molded composites absorbed less than did extruded composites, and injection-molded composites absorbed the least. Although more moisture was absorbed during water soaking, the cyclic boiling procedure caused more damage to the composites, especially the extruded ones. In neither procedure for infusing water did the composites reach equilibrium. A standard method for determining the durability of structural wood was modified for testing the fungal resistance of composites. Moisture content, flexural properties, and weight loss were measured over a 12-week exposure to the brown-rot fungus Gloeophyllum trabeum. Significant weight losses were found once the composite moisture content reached roughly 12 to 15 percent. This corresponds to an average wood flour moisture content near the fiber saturation point. The greatest weight losses were found for extruded composites that had been preconditioned by boiling. Damage to the composite from moisture sorption complicated the use of flexural performance as a measure of fungal attack. Mechanical performance appeared to be a less sensitive measure of fungal attack than was weight loss. However, flexural modulus loss and strength loss due to fungal attack correlated well with weight loss for individual specimens when the data were plotted together.

Keywords: Fungal resistance, high density polyethylene, wood-HDPE composites, brown-rot fungus, Gloeophyllum trabeum.

Publication Notes:

  • We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
  • This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.

XML: View XML

Citation:


Clemons, Craig M.; Ibach, Rebecca E. 2004. Effects of processing method and moisture history on laboratory fungal resistance of wood-HDPE composites. Forest products journal. Vol. 54, no. 4 (Apr. 2004): Pages 50-57.

 