Skip to page content
USDA Forest Service
  
Treesearch

Research & Development Treesearch

 
Treesearch Home
About Treesearch
Contact Us
Research & Development
Forest Products Lab
International Institute of Tropical Forestry
Northern
Pacific Northwest
Pacific Southwest
Rocky Mountain
Southern
Help
 

GeoTreesearch


Science.gov - We Participate


USA.gov  Government Made Easy


Global Forest Information Service

US Forest Service
P.O. Box 96090
Washington, D.C.
20090-6090

(202) 205-8333

You are here: Home / Search / Publication Information
Bookmark and Share

Publication Information

(119 KB bytes)

Title: Yield and ultrasonic modulus of elasticity of red maple veneer

Author: Ross, Robert J.; Verhey, Steven; Erickson, John R.; Forsman, John W.; Brashaw, Brian K.; Pilon, Crystal L.; Wang, Xiping

Date: 2004

Source: Forest products journal. Vol. 54, no. 12 (Dec. 2004): Pages 220-225

Publication Series: Not categorized

Description: The purpose of the study was to assess the potential for using red maple sawlogs to manufacture laminated veneer lumber (LVL). The primary objective was to determine the yield of ultrasonically graded veneer from red maple logs. A sample of 48 logs was obtained from six Eastern and Lake States in the United States. The logs were visually graded and shipped to a plywood manufacturing facility in northern Michigan where they were debarked, steamed for 72 hours,and then rotary peeled into nominal 1/8- inch- (standard 3-mm-) thick veneer. Special care was taken to ensure that each veneer sheet could be traced back to the log from which it came. The veneer sheets were dried to approximately 12 percent moisture content at the plywood mill, shipped to theUSDAForest Service, Forest Products Laboratory in Madison, Wisconsin, and nondestructively tested using a commercially available ultrasonic veneer grader. The average stresswave speed, obtained from the veneer grader, and the density of each sheet was used to compute its modulus of elasticity (MOE). Veneer yield and MOE were compared on the basis of geographical region of log origin: Lake States (Michigan and Wisconsin) and Eastern States (New York, Pennsylvania, Vermont, and West Virginia). Veneer yield was tabulated based on four categories: 54-inch- (137-cm-) wide sheets, 36-inch- (91-cm-) wide sheets, strips, and fishtails. The only major difference in yield between the two regions was observed in the No. 2 logs. The Eastern States’No. 2 logs yielded approximately 13 percent more of the original log volume as 54- inch (137-cm) sheets. TheMOEcomparisons were based on results from the 54- inch (137-cm) sheets because the yield of 36-inch (91-cm) sheets was low. When grouped, the yield of 54-inch (137-cm) veneer sheetswas similar for the No. 1 and No. 2 logs, but lower from the No. 3 logs. Decreases in the total veneer yield corresponded with decreases in log quality. The MOE values of veneer from all logs had a mean value of 1.80 × 106 lb./in.2 (12.4 GPa) and a standard deviation of 0.33 × 106 lb./in.2 (2.3 GPa).

Keywords: Yield, ultrasonic modulus of elasticity, red maple, veneer, modulus of elasticity

Publication Notes:

  • We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
  • This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.

XML: View XML

Citation:


Ross, Robert J.; Verhey, Steven; Erickson, John R.; Forsman, John W.; Brashaw, Brian K.; Pilon, Crystal L.; Wang, Xiping 2004. Yield and ultrasonic modulus of elasticity of red maple veneer. Forest products journal. Vol. 54, no. 12 (Dec. 2004): Pages 220-225

 


 [ Get Acrobat ]  Get the latest version of the Adobe Acrobat reader or Acrobat Reader for Windows with Search and Accessibility

USDA logo which links to the department's national site. Forest Service logo which links to the agency's national site.