Skip to page content
USDA Forest Service
  
Treesearch

Research & Development Treesearch

 
Treesearch Home
About Treesearch
Contact Us
Research & Development
Forest Products Lab
International Institute of Tropical Forestry
Northern
Pacific Northwest
Pacific Southwest
Rocky Mountain
Southern Research Station
Help
 

Science.gov - We Participate


USA.gov  Government Made Easy


Global Forest Information Service

US Forest Service
P.O. Box 96090
Washington, D.C.
20090-6090

(202) 205-8333

You are here: Home / Search / Publication Information
Bookmark and Share

Publication Information

View PDF (2.77 MB bytes)

Title: Atomic force microscopy of the intervessel pit membrane in the stem of Sapium sebiferum (Euphorbiacea)

Author: Pesacreta, Thomas C.; Groom, Leslie H.; Rials, Timothy G.;

Date: 2005

Source: IAWA Journal, Vol. 26(4): 397-426

Publication Series: Miscellaneous Publication

Description: Sapwood and juvenile wood of Sapium sebiferum (Euphorbiacea) was collected during 2000-2002. In air-dried vessel elements, the surface of pit membranes (PMs) in the outermost growth ring was coated with plaque-like or interstitial material that was 2-5 nm thick. This coating was phase dark and overlaid a phase bright layer of globules and reticulately arranged microfibrils (MFs) that was 25-50 nm thick. Beneath the reticulate layer there was another surface exposed during sectioning / fracturing. It had parallel MFs which appeared to be continuous with the middle lamella, and were also coated. The total thickness of the dried PM appeared to be in the range of 0-100 nm. Overwintering and heartwood PMs were encrusted with a non-microfibrillar layer that differed from the above mentioned coating. Prior chemical treatment, specified dried, untreated PMs were located and then the sample was dismounted, treated with acidic H2O2, and observed after treatment so that before and after images could be compared. Treatment with acidic H2O2 removed some of the coating and greatly modified the fibrillar nature of the surface layer, but did not reduce its overall thickness. The native structure of sapwood PMs was observed in water. Non-dried PMs displayed two layers, each with a different type of surface. The outer layer was non-microfibrillar and covered the entire surface of the PM. The non-microfibrillar layer was extremely sensitive to mechanical perturbation by the AMF tip, and has phase characteristics similar to the coating of dried PMs. The underlying layer was thick and microfibrillar. The MFs in non-dried PMs were, like dried MFs, phase bright but they were much more loosely intermeshed compared with those seen in dried materials. The measurable thickness (which does not represent the total thickness) of non-dried PMs frequently ranged from 90-225 nm, although a few 500 nm vertical features were measured.

Keywords: Atomic force microscopy, cellulose microfibril, Euphorbiaceae, pit membrane, Sapium, transpiration, vessel, wood structure, xylem

Publication Notes:

  • We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
  • This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.
  • You may send email to pubrequest@fs.fed.us to request a hard copy of this publication. (Please specify exactly which publication you are requesting and your mailing address.)

XML: View XML

Citation:


Pesacreta, Thomas C.; Groom, Leslie H.; Rials, Timothy G. 2005. Atomic force microscopy of the intervessel pit membrane in the stem of Sapium sebiferum (Euphorbiacea). IAWA Journal, Vol. 26(4): 397-426

 