Skip to page content
USDA Forest Service

Research & Development Treesearch

Treesearch Home
About Treesearch
Contact Us
Research & Development
Forest Products Lab
International Institute of Tropical Forestry
Pacific Northwest
Pacific Southwest
Rocky Mountain
Southern Research Station
Help - We Participate  Government Made Easy

Global Forest Information Service

US Forest Service
P.O. Box 96090
Washington, D.C.

(202) 205-8333

You are here: Home / Search / Publication Information
Bookmark and Share

Publication Information

View PDF (307 KB)

Title: Improvement of water resistance and dimensional stability of wood through titanium dioxide coating

Author: Sun, Qingfeng; Yu, Haipeng; Liu, Yixing; Li, Jian; Lu, Yun; Hunt, John F.;

Date: 2010

Source: Holzforschung. Vol. 64, no. 6 (Oct. 2010): p. 757-761.

Publication Series: Scientific Journal (JRNL)

Description: Moisture absorption and dimensional distortion are the major drawbacks of wood utilization as building material. In this study, poplar wood coated with a thin layer of titanium dioxide (TiO2) was prepared by the cosolvent-controlled hydrothermal method. Subsequently, its moisture absorption and dimensional stability were examined. Scanning electron microscopy analysis revealed that the wood substrate was closely and entirely covered with the TiO2 coat. Microscale features were visible despite masking of the ultrastructural features of the cell wall. To explore the effects of TiO2 coating on the water-repellency and dimensional stability of wood, a 90-day water immersion test was carried out. Results showed that water absorption and thickness swelling of TiO2 coated wood increase very slowly and minimally. Weight change after 90 days of water immersion was reduced to 20.5%, nearly one-tenth of untreated control wood, and that maximum cross-sectional relative swelling was only 1.2%. Specimens were conditioned for 3 months at 20%, 30%, 40%, 50%, 60%, 70%, 80%, and 90% relative humidity (RH) to determine the effects of RH on moisture absorption and dimensional swelling of TiO2-coated wood. There was no change in weight after 3 months of being exposed to humidity conditions below 60%, whereas there was linear weight increase above 60% RH, but the maximum change was less than 6%. Cross-sectional relative swelling was less than 0.3% below 60% RH but increased as RH exceeded 60%. The maximum change was approximately 3%. Anisotropic thickness swelling of wood was almost eliminated after coating. It is obvious that TiO2 coating can act as a moisture barrier for wood and is an exceptionally strong water vapor-inhibiting shield under very humid conditions.

Keywords: Titanium dioxide, coatings, testing, moisture, building materials, weathering, absorption, deterioration, water repellents, poplar, scanning electron microscopy, humidity, anisotropy, moisture content, dimensional stability, swelling, Populus ussuriensis, weight of wood, hydrothermal method

Publication Notes:

  • We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
  • This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.



Sun, Qingfeng; Yu, Haipeng; Liu, Yixing; Li, Jian; Lu, Yun; Hunt, John F. 2010. Improvement of water resistance and dimensional stability of wood through titanium dioxide coating. Holzforschung. 64(6): 757-761.