Title: Carboxymethylated-, hydroxypropylsulfonated- and quaternized xylan derivative films
Author: Simkovic, Ivan; Kelnar, Ivan; Uhliarikova, Iveta; Mdndichi, Raniero; Mandalika, Anurag; Elder, Thomas;
Source: Carbohydrate Polymers. 110:464-471.
Publication Series: Scientific Journal (JRNL)
Description: Under alkaline/water conditions carboxymethyl, 2-hydroxypropylsulfonate and trimethylammonium-2-hydroxypropyl groups were introduced into xylan in one step with the goal to prepare film specimens. The materials were characterized by NMR, SEC-MALS, TG/DTG/DTA, AFM and mechanical testing. The properties of triple, double and mono-substituted materials were compared. The numerical molar masses of the specimens were from 12.3 to 17.6 kg/mol with Mw/Mn from 1.27 to 1.34. The elastic modulus values are decreasing in order: xylan (X; 7354 MPa) > carboxymethyl xylan (CX; 6090 MPa) > 2-hydroxypropylsulfonate xylan (SX; 6000 MPa) > carboxymethyl/2-hydroxypropylsulfonate xylan (CSX;4490 MPa) > quaternized xylan (QX; 3600 MPa) > carboxymethyl/quaternary/2-hydroxypropylsulfonatexylan (CQSX; 3380 MPa) > carboxymethyl/quaternary xylan (CQX; 2805 MPa). The onset temperatures of SX (214◦C), CQSX (212◦C), QSX (211◦C) and CQX (207◦C) were higher than for X (205◦C). The roughness values of the film surfaces (3.634 – 18.667 nm) are higher on top than on the bottom of the specimen.
Keywords: Xylan, Films, Properties, Molar masses, AFM
- We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
- This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.
XML: View XML
Simkovic, Ivan; Kelnar, Ivan; Uhliarikova, Iveta; Mdndichi, Raniero; Mandalika, Anurag; Elder, Thomas 2014. Carboxymethylated-, hydroxypropylsulfonated- and quaternized xylan derivative films. Carbohydrate Polymers 110:464-471.
Get the latest version of the Adobe Acrobat reader or Acrobat Reader for Windows with Search and Accessibility