Skip to page content
USDA Forest Service
  
Treesearch

Research & Development Treesearch

 
Treesearch Home
About Treesearch
Contact Us
Research & Development
Forest Products Lab
International Institute of Tropical Forestry
Northern
Pacific Northwest
Pacific Southwest
Rocky Mountain
Southern Research Station
Help
 

Science.gov - We Participate


USA.gov  Government Made Easy


Global Forest Information Service

US Forest Service
P.O. Box 96090
Washington, D.C.
20090-6090

(202) 205-8333

You are here: Home / Search / Publication Information
Bookmark and Share

Publication Information

View PDF (2.0 MB bytes)

Title: Fatigue behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP)

Author: Li, Jinghao; Hunt, John F.; Gong, Shaoqin; Cai, Zhiyong;

Date: 2015

Source: Holzforschung

Publication Series: Scientific Journal (JRNL)

Description: The static and fatigue bending behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP) has been investigated by four-point bending tests. Fatigue panels and weakened panels (wESCP) with an initial interface defect were manufactured for the fatigue tests. Stress σ vs. number of cycles curves (S-N) were recorded under the different stress levels. The primary failure mode in the fatigue tests was observed in the shear zone (epoxy debonding), which was different from face failure in the pure bending zone for the static bending test. For residual bending (RB) test, epoxy debonding failure occurred between the pure bending zone and shear zone. Macro cracks along the core/face interface developed as the number of cycles increased during the fatigue life. The crack propagation or damage for the panels submitted to fatigue test can be described as a three-stage damage process of first non-linear portion, followed by linear damage accumulation, and lastly nonlinear accelerated damage. Bending stiffness degradation at the higher load level had faster degradation during fatigue life. The dissipated energy of the panels was small due to the high stiffness of the materials.

Keywords: bending stiffness, fatigue behavior, residual properties, sandwich panel, S-N curve, static testing, wood-fiber-composite

Publication Notes:

  • We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
  • This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.

XML: View XML

Citation:


Li, Jinghao; Hunt, John F.; Gong, Shaoqin; Cai, Zhiyong. 2016. Fatigue behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP). Holzforschung. 70(6): 9 p.

 