Skip to page content
USDA Forest Service
  
Treesearch

Research & Development Treesearch

 
Treesearch Home
About Treesearch
Contact Us
Research & Development
Forest Products Lab
International Institute of Tropical Forestry
Northern
Pacific Northwest
Pacific Southwest
Rocky Mountain
Southern Research Station
Help
 

Science.gov - We Participate


USA.gov  Government Made Easy


Global Forest Information Service

US Forest Service
P.O. Box 96090
Washington, D.C.
20090-6090

(202) 205-8333

You are here: Home / Search / Publication Information
Bookmark and Share

Publication Information

View PDF (213 KB bytes)

Title: Durability of structural lumber products at high temperatures. Part I, 66C at 75% RH and 82C at 30% RH

Author: Green, David W.; Evans, James W.; Craig, Bruce A.;

Date: 2003

Source: Wood and fiber science. Vol. 35, no. 4 (2003): Pages 499-523.

Publication Series: Miscellaneous Publication

Description: The effect of temperature on properties can be separated into reversible and permanent effects. The National Design Specification (NDS) provides factors (Ct) for reducing properties for reversible effects but provides little guidance on permanent effects. The primary objective of this paper is to evaluate the effect of prolonged heating (permanent effect) on the flexural properties of solid-sawn and composite lumber products exposed at 66°C and 75% relative humidity (RH) and at 82°C and 30% RH. A second objective is to determine how to estimate total effects. Solid-sawn lumber, laminated veneer lumber (LVL), and laminated strand lumber (LSL) were heated continuously for up to 6 years. After each exposure period, the lumber was conditioned to room temperature at the specified RH and then tested on edge in third-point bending. Some lumber was also tested hot at 66°C after 48 h of exposure and after 3 years of exposure. After 3 years of continuous exposure at 66°C and 75% RH, solid-sawn Spruce-Pine- Fir (SPF) and Douglas-fir retained about 72% of their original modulus of upture (MOR) and southern pine about 47%. For the first 2 to 3 years of exposure, changes in MOR of LVL were similar to that of solid-sawn SPF and Douglas-fir. After almost 6 years of exposure, SPF retained about 67% MOR and LVL 26% to 49%. The MOR of LSL was more sensitive to duration of exposure than was the MOR of either solid-sawn lumber or LVL, with a residual MOR of 47% after 28 months. After 21 months at 82°C and 30% RH, solid-sawn lumber retained 50% to 55% MOR, LVL 41%, and LSL 45%. For all products, modulus of elasticity was less sensitive to thermal degradation than was MOR. The effect of temperature on MOR of solid-sawn lumber is independent of grade. Composite lumber is more sensitive than solid-sawn to change in strength due to thermal degradation. The difference in MOR between species and product types may be less at low humidity levels than at high. The total effect of temperature on MOR can be estimated by adding the reversible plus the permanent effects. Available literature suggests that the wood used in attics of residential construction is not likely to experience significant accumulation of exposure at temperatures ³66°C over the life of the structure.

Keywords: Lumber, laminated veneer lumber, laminated strand lumber, modulus of rupture, modulus of elasticity, long-term temperature exposure.

Publication Notes:

  • We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
  • This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.

XML: View XML

Citation:


Green, David W.; Evans, James W.; Craig, Bruce A. 2003. Durability of structural lumber products at high temperatures. Part I, 66C at 75% RH and 82C at 30% RH. Wood and fiber science. Vol. 35, no. 4 (2003): Pages 499-523.

 