Skip to page content
USDA Forest Service

Research & Development Treesearch

Treesearch Home
About Treesearch
Contact Us
Research & Development
Forest Products Lab
International Institute of Tropical Forestry
Pacific Northwest
Pacific Southwest
Rocky Mountain
Southern Research Station
Help - We Participate  Government Made Easy

Global Forest Information Service

US Forest Service
P.O. Box 96090
Washington, D.C.

(202) 205-8333

You are here: Home / Search / Publication Information
Bookmark and Share

Publication Information

View PDF (263 KB bytes)

Title: Effects of wood fiber characteristics on mechanical properties of wood/polypropylene composites

Author: Stark, Nicole M.; Rowlands, Robert E.;

Date: 2003

Source: Wood and fiber science. Vol. 35, no. 2 (2003): Pages 167-174

Publication Series: Miscellaneous Publication

Description: Commercial wood flour, the most common wood-derived filler for thermoplastics, is produced in a mixture of particle sizes and generally has a lower aspect ratio than wood and other natural fibers. To understand how wood flour and fiber characteristics influence the mechanical properties of polypropylene composites, we first investigated the effect of different sizes of wood flour particles on the mechanical properties of wood-flour-filled polypropylene composites. We then compared the properties of wood-flour-filled composites to those of composites reinforced with refined wood fiber. We also studied the effect of a maleated polypropylene coupling agent on composite properties. Wood flour particles (35, 70, 120, and 235 mesh) were compounded at 40% by weight with polypropylene. Increases in tensile and flexural strength and modulus of the wood flour composites were found to correspond with increases in aspect ratio. Notched impact energy increased with increasing particle size, whereas unnotched impact energy decreased with increasing particle size. Refined wood fiber and 40-mesh wood flour was compounded at 20% and 40% by weight with polypropylene. Wood fiber resulted in higher strengths at both filler levels and higher moduli at the 40% level compared to the strength properties of wood flour composites. The higher aspect ratio of the wood fiber had little effect on impact energy. The maleated polypropylene coupling agent caused greater strength increases in wood fiber composites than in wood flour composites. The coupling agent did not significantly affect tensile or flexural moduli. Our results clearly support the use of higher aspect ratio wood fibers and coupling agents for increasing the strength of wood/plastic composites.

Keywords: Wood flour, wood fiber, polypropylene, mechanical properties, aspect ratio, coupling agent

Publication Notes:

  • We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
  • This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.



Stark, Nicole M.; Rowlands, Robert E. 2003. Effects of wood fiber characteristics on mechanical properties of wood/polypropylene composites. Wood and fiber science. Vol. 35, no. 2 (2003): Pages 167-174